Organic Compound Base is combined by glass fiber mesh and polyester-cotton non-woven by strong adhesive with high-temperature drying to get the finished roll .Compound Base has high tensile strength, especially in vertical direction (machine direction), it is meanly used to be used as the base reinforcement of bitumen waterproof membrane and asphalt shingles .it is easy to be coated by hot bitumen .with competitive price compared to polyester mat . Welcomed by waterproof materials factories all over the world.
(ONLY FOR YOUR REFERENCE)Customized Technical data: Fiberglass mesh + Poly-cotton mat
Item |
Unit Weight (G/M2) |
Moisture Content |
Shrinkage |
Tensile Strength (N/cm) |
Roll width |
Loading Capacity |
|
longitudinal |
Transversal |
CM |
M2/40'HC |
||||
CH-4*4 |
70g |
≤0.5% |
≤0.5% |
250 |
110 |
100 |
About 175500sqms |
CH-5*5 |
85g |
≤0.5% |
≤0.5% |
350 |
200 |
100 |
About 163800sqms |
CH-6*6 |
95-105g |
≤0.5% |
≤0.5% |
450 |
300 |
100 |
About 146250sqms |
CH-7*7 |
100-110g |
≤0.5% |
≤0.5% |
550 |
400 |
100 |
About 140400sqms |
CH-8*8 |
110g-120g |
≤0.5% |
≤0.5% |
650 |
500 |
100 |
About 140000sqms |
Packing |
Paper roll in core,then seaworthy plastic bag,then woven bag outside. |
||||||
Width |
100cm |
Organic Compound Base show and Application:
Should you have any preference for the nonwoven combination mat substrate for modified asphalt waterproof membrane production, welcome to contact us for the product made in China. As a leading such manufacturer in China, we are equipped with a professional factory at your service, and we will offer you the most competitive price.